Prussian blue analogues (PBAs) have high theoretical specific capacity, long cycle life, environmental benignity, and low cost, which are promising as cathode materials for sodium-ion batteries (SIBs). However, the working mechanism of PBAs is still unclear which hinders their applications.
Recently, Our group in collaboration with Prof. LI Xianfeng from DICP, and Dr. Moulay Tahar Sougrati from the University of Montpellier, revealed the charging/discharging mechanism and capacity degradation principle of Prussian blue cathode in SIBs through operando Mössbauer spectroscopy, which provides a new strategy for optimizing the cathode materials.
Operando Mössbauer spectroscopy firstly applied into Sodium-ion battery with Prussian blue cathode
This study was published in Nano Energy on Feb.5.
Schematic diagram of HS/LS Fe redox mechanism and local structure changes in the electrochemical reaction process (Image by WANG Zinan)
The researchers synthesized a sodium-rich Prussian blue by co-precipitation method, and used it as a cathode for SIB. The SIB showed good electrochemical performance, which could maintain 81% capacity retention after 980 cycles under 120mAg-1.
Furthermore, they on-line observed the working process of the SIB through operando Mössbauer spectroscopy, and revealed the working mechanism of Prussian blue using low-temperature 77K 57Fe Mössbauer spectroscopy, operando X-ray diffraction spectroscopy, and synchrotron X-ray absorption spectroscopy combined with the operando Mössbauer spectroscopy.
They found the reaction of high-spin (HS) Fe and low-spin (LS) Fe reacted stepwise. The HS Fe reacted completely and contributed to most capacity, while only part of LS Fe reacted, which could be ascribed to the main reason for discrepancy between practical capacity and theoretical one. However, the LS Fe could lead to more severe local distortions with respect to the effects imposed by the same amount of HS Fe, which was harmful to the cycling stability. Therefore, the good cycling performance for the PB cathode material can be both assigned to the tiny changes of crystal parameters and the incomplete reaction of LS Fe.
“This work provides new insight into developing PBAs cathode materials with high capacity and excellent cycling stability,” said Prof. WANG.
This work was supported by theNational Natural Science Foundation of China, the International Partnership Program of Chinese Academy of Sciences, the President's International Fellowship Initiative (PIFI) of Chinese Academy of Sciences.
Link: https://doi.org/10.1016/j.nanoen.2023.108256